HomeInteraction Parameters

The interaction parameters are used to correct the activity factors for each element based on the composition of the solution.

These values are defined for a solution at the reference temperature of 1873K.

The program will scale these parameters to the required temperature before using them.

All elements in this matrix are supported by this program and can have their activity calculated.

This website supports non-symmetrical interaction parameters. While most of the non-symmetrical terms are due to rounding errors, some may be due to reported literature values and should be investigated carefully. To highlight non-symmetric terms in the matrix below, please click these links to highlight those interaction parameters different by: 100%, 50%, 10%, 1%, 0.1%.

Interaction Parameters Matrix ( $ε_{i}^{j}$ )

	Ag	Al	As	B	Bi	C	Ca	Cd	Ce	Co	Cr	Cu	Ga	Ge	H	Hf	In	La	Mn	Mo	N	Nb	Ni	O	P	Pb	Re	S	Sb	Si	Sn	Ta	Ti	Tl	U	V	W	Zn	Zr
Ag	-18.732	-8.388				11.686					-2.012													-5.821
Al	-8.497	5.303				5.294	-7.517								1.98						1.685			-129.981	4.662	2.77		4.921		6.986					7.54
As						7.63															5.199							0.891
B				2.435		11.686									3.394				-0.179		4.968			-13.148	1.311			6.595		9.535
Bi						3.06
C	11.529	5.303	12.95	11.689	3.06	12.826	-15.756	18.83	-3.012	1.721	-4.865	3.97	11.56	2.097	3.768		5.49	2.295	-1.857	-6.009	7.106	-22.781	2.307	-20.409	6.962	5.599	0	6.08	6.355	9.767	9.391	-170.224		8.24		-6.051	-6.399	-3.94
Ca		-7.526				-16.063	-0.048																-10.745	-38283.417				-18519.804		-10.666
Cd						18.83
Ce						-3.031			0.746						-1.513				29.481					-36963.274				-5291.068
Co						1.729				1.182	-4.725		0	0	0.4		0		-0.921		2.887			1.902	0.918	-0.058	0	0.556		4.6
Cr	-1.999					-2.89				-4.75	0.005	4.057	0	0	-0.432		0		0.886	-0.005	-9.768		-0.002	-9.848	-3.772	4.385	0	-22.063		0.03	3.195					2.61
Cu						4.99					3.93	-5.381	0	0	0.192		0				2.201			-3.577	-8.277	-7.297	0	-2.289		3.626	-6.513
Ga						11.56				0	0	0	0	0		0			0	0		0	0	0	0		0	0		0		0	0			0	0		0
Ge						7.1				0	0	0	0	0	2.687	0			0	0		0	0	0	0		0	0		0		0	0			0	0		0
H		1.964		3.393		3.758			-1.509	0.382	-0.446	0.203		2.696	0.982			-16.96	-0.437	0.43		-1.928	-0.511	4.014	2.362			2.675		3.626	1.666	-0.971	-3.609			-1.467	1.349		-3.945
Hf													0	0		2.959	0							-210.509			0	-35.292
In						5.49				0	0	0				0	0		0	0		0	0	0	0		0	0		0		0	0			0	0		0
La						2.271									-16.899			-5.957	63.479					-2958.793				-10506.07
Mn				-0.246		-1.881			29.707	-0.916	0.891		0	0	-0.432		0	61.55	0.016	1.085	-4.509	2.1	-1.766	-4.765	-6.451	-5.05	0	-5.766		-3.292		0.367	-9.731			1.265	3.044
Mo						-6.021					0.005		0	0	0.441		0		1.087	3.963	-5.029			1.261	-0.321	-0.744	0	0.347		22
N		1.7	5.222	4.999		7.227				2.862	-9.799	2.229							-4.517	-5.072	0.749	-26.728	1.644	-7.207	7.985			1.337	3.24	6.059	2.31	-45.538	-118.345			-23.24	-3.821		-237.736
Nb						-22.799							0	0	-1.929		0		2.09		-26.699	-0.663		-46.812	-5.305		0	-5.508		0
Ni						2.307	-10.67				0.005		0	0	-0.515		0		-1.768		1.616		0.119	1.374	0.675	-4.551	0	-0.049		7.5
O	-5.827	-129.722		-13.02		-20.076	-85152.798		-36997.511	1.89	-11.729	-3.546	0	0	4.018	-208.382	0	-2989.278	-4.743	1.261	-7.341	-46.659	1.402	-10.508	9.39		0	-17.168	-12.734	-7.15	-6.562	-76.892	-221.035		-435.347	-29.335	4.155		-1506.048
P		4.636		1.318		7.028				0.917	-3.792	-8.319	0	0	2.354		0		-6.464	-0.322	8.261	-5.263	0.676	9.294	7.346	6.157	0	4.792		11.968	5.101		-7.756			-4.956	-17.629
Pb		2.778				8.75				-0.054	4.359	-7.279							-5.058	-0.718			-4.527		6.052			-38.55		5.9	26.075						-2.23
Re						0				0	0	0	0	0		0	0		0	0		0	0	0	0		0	0		0		0	0			0	0		0
S		4.945	0.901	6.602		6.117	-18187.754		-5261.878	0.562	-2.125	-2.278	0	3.791	2.687	-35.333	0	-10544.637	-5.72	0.351	1.313	-2243.87	-0.05	-17.108	4.787	-38.666	0	-5.659	0.66	8.942	-3.193	-16.424	-35.403		-69.057	-3.801	5.896		-79.668
Sb						17.57															3.234			-12.488				0.659
Si		6.973		9.727		9.704	-10.67			4.6	0.03	3.637	0	0	3.643		0		-3.24	22	6.066	0	7.5	-7.141	11.946	5.9	0	8.912		8.6	7.008	27.621	243.043			2	18.3
Sn						8.37					3.199	-6.43			1.647						2.309			-6.547	4.911	26.483		-3.191		6.912	-0.293
Ta						-168.958							0	0	-0.972		0		0.373		-38.834			-78.495			0	-16.771		27.147		79.877
Ti													0	0	-3.592		0		-9.73		-118.29			-223.711	-7.222		0	-35.292		243.823			8.437
Tl						8.24
U		7.084																						-434.933				-69.686							9.504
V						-4.72					2.622		0	0	-1.471		0		1.265		-22.365			-29.65	-4.922		0	-3.834		2						6.582
W						-6.506							0	0	1.348		0		3.049		-3.828			4.146	-17.865	-2.222	0	5.951		18.3
Zn						-3.94
Zr													0	0	-4.008		0				-237.907			-1517.45			0	-80.269											11.41

Interaction Parameter Orphans

The following elements are not shown in the matrix above because they do not have a gamma zero defined.

For completeness they are included in the large table below.

The interaction parameter orphans are:

Interaction Parameters - Table

Decimal Places:

i	j	$ε_{i}^{j}$	Reference	Source
Ag	Ag	-18.73223202	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ag	Al	-8.388309558	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ag	C	11.68624221	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ag	Cr	-2.011791971	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ag	O	-5.821175862	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Al	Ag	-8.496748565	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
C	Ag	11.52919733	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	Ag	-1.999441674	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Ag	-5.826622446	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
As	C	13.17278244	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
As	N	5.198733532	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
As	S	0.890901066	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
C	As	12.94967204	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	As	5.222258667	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	As	0.90110202	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
As	C	7.63	Voisin, L., H. M. Henao, et al. (2005). "Phase Relations, Activities and Minor Elements Distribution in Fe–Pb–As and Fe–Pb–Sb Systems Saturated with Carbon at 1473 K." MATERIALS TRANSACTIONS 46(12): 3030-3036.	ips_05_voisin2005.csv

i	j	$ε_{i}^{j}$	Reference	Source
Au	O	-8.299825854	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Au	S	-0.242151088	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Au	-7.99564423	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Au	-0.244700573	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
B	B	2.434526054	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	C	11.68624221	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	H	3.393799803	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	Mn	-0.178592403	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	N	4.967589379	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	O	-13.14796627	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	P	1.310973128	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	S	6.594788613	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	Si	9.53494973	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
C	B	11.68928153	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	B	3.393335754	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	B	-0.24617594	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	B	4.999002678	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	B	-13.02014836	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	B	1.31790581	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	B	6.602001836	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	B	9.726799731	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
Be	O	-85.09572792	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Be	-88.39493818	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
Al	Ca	-7.51684095	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
C	Ca	-15.75614207	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ca	Al	-7.525810962	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ca	C	-16.06250877	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ca	Ca	-0.04829229	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ca	Ni	-10.74532153	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ca	O	-38283.41653	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ca	S	-18519.80401	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ca	Si	-10.66606291	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	Ca	-10.67015196	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Ca	-85152.79798	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Ca	-18187.75419	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Ca	-10.67015196	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	Ce	-3.011753999	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ce	C	-3.030506079	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ce	Ce	0.745652484	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ce	H	-1.513061482	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ce	Mn	29.48113873	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ce	O	-36963.27411	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ce	S	-5291.068378	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Ce	-1.508791406	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	Ce	29.70658553	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Ce	-36997.51109	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Ce	-5261.877868	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	Co	1.721100713	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	C	1.728564123	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	Co	1.182351081	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	Cr	-4.724812365	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	H	0.399782748	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	Mn	-0.920625603	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	N	2.887292006	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	O	1.90165727	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	P	0.918217379	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	Pb	-0.058380864	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	S	0.556135656	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	Co	-4.749641769	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Co	0.382437671	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	Co	-0.915586375	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Co	2.862412377	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Co	1.889873277	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Co	0.917334176	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Co	-0.053731221	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Co	0.56154385	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Co	4.6	Tuff, J, Wood, BJ, Wade, J,"The effect of Si on metal-silicate partitioning of siderophile elements and implications for the conditions of core formation", GEOCHIMICA ET COSMOCHIMICA, 2011, 10.1016/j.gca.2010.10.027, Table 5	ips_03_tuff_et_al.csv
Co	Si	4.6	Tuff, J, Wood, BJ, Wade, J,"The effect of Si on metal-silicate partitioning of siderophile elements and implications for the conditions of core formation", GEOCHIMICA ET COSMOCHIMICA, 2011, 10.1016/j.gca.2010.10.027, Table 5	ips_03_tuff_et_al.csv
Ga	Co	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Re	Co	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Co	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
In	Co	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	Cu	3.970209617	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	Cu	4.056848124	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	C	3.96872948	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	Cr	3.930276234	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	Cu	-5.381104918	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	H	0.191864897	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	N	2.200887395	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	O	-3.576933755	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	P	-8.276816573	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	Pb	-7.296821017	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	S	-2.289370321	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	Si	3.625603596	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	Sn	-6.512764193	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Cu	0.203017299	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Cu	2.22880759	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Cu	-3.545947382	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Cu	-8.319075438	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Cu	-7.278790128	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Cu	-2.277520439	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Cu	3.637383545	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Sn	Cu	-6.429766367	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ga	Cu	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Re	Cu	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Cu	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
In	Cu	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Cu	C	4.99	Revised epsilon values from high pressure experiments, A. Norris DPhil thesis 2016.	ips_08_corrections_norris.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	Ge	2.096841853	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ge	C	2.271487411	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ge	Ge	1.797158287	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ge	H	2.686879109	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ge	S	3.762158228	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Ge	2.696208986	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Ge	3.790967191	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ga	Ge	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Re	Ge	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	O	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Si	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	P	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	S	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Ti	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	V	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Cr	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Mn	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Co	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Ni	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Ge	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Zr	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Nb	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Mo	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Hf	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Ta	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	W	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Re	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Cu	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	C	7.10	Revised epsilon values from high pressure experiments, A. Norris DPhil thesis 2016.	ips_08_corrections_norris.csv

i	j	$ε_{i}^{j}$	Reference	Source
Al	H	1.979958416	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	H	3.393799803	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
C	H	3.768051935	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ce	H	-1.513061482	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	H	0.399782748	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	H	-0.431888657	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	H	0.191864897	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ge	H	2.686879109	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Al	1.963988152	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	B	3.393335754	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	C	3.758027642	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Ce	-1.508791406	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Co	0.382437671	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Cr	-0.445831758	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Cu	0.203017299	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Ge	2.696208986	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	H	0.981952731	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	La	-16.95996283	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Mn	-0.436976122	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Mo	0.430033541	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Nb	-1.928370278	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Nd	-24.19588876	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Ni	-0.510987776	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	O	4.013885135	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	P	2.362191778	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Pd	0.894628882	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Rh	1.534929102	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	S	2.67475793	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Si	3.625603596	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Sn	1.666059928	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Ta	-0.97080892	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Ti	-3.609185153	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	V	-1.467328179	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	W	1.348887119	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Zr	-3.945287781	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
La	H	-16.89898246	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	H	-0.431888657	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	H	0.441366318	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	H	-1.928897184	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	H	-0.515055797	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	H	4.017553356	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	H	2.354210548	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pd	H	0.894627233	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Rh	H	1.522539143	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	H	2.686879109	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	H	3.643301224	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Sn	H	1.647289854	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ta	H	-0.972475069	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ti	H	-3.592239993	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
V	H	-1.471477912	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
W	H	1.347888148	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Zr	H	-4.008075695	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
Hf	Hf	2.958766281	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Hf	O	-210.5092574	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Hf	S	-35.29171332	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Hf	-208.3818061	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Hf	-35.33290537	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ga	Hf	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Re	Hf	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Hf	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
In	Hf	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	La	2.295134524	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	La	-16.95996283	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
La	C	2.271487411	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
La	H	-16.89898246	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
La	La	-5.957050055	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
La	Mn	63.47899651	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
La	O	-2958.792565	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
La	S	-10506.06959	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	La	61.55040435	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	La	-2989.277633	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	La	-10544.63749	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	Mg	7.583905623	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mg	C	8.217648334	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mg	O	-197.3078333	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Mg	-197.9751338	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	Mo	-6.00927778	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	Mo	-0.005357504	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Mo	0.430033541	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	Mo	1.085245198	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	C	-6.020852618	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	Cr	0.004649947	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	H	0.441366318	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	Mn	1.086573069	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	Mo	3.962797025	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	N	-5.02939522	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	O	1.261388198	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	P	-0.321300468	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	Pb	-0.743841511	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	S	0.34650046	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	Si	933.2468591	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Mo	-5.071726027	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Mo	1.261234627	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Mo	-0.322005537	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Mo	-0.717815577	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Mo	0.350871533	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Mo	933.3938809	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Mo	22	Tuff, J, Wood, BJ, Wade, J,"The effect of Si on metal-silicate partitioning of siderophile elements and implications for the conditions of core formation", GEOCHIMICA ET COSMOCHIMICA, 2011, 10.1016/j.gca.2010.10.027, Table 5	ips_03_tuff_et_al.csv
Mo	Si	22	Tuff, J, Wood, BJ, Wade, J,"The effect of Si on metal-silicate partitioning of siderophile elements and implications for the conditions of core formation", GEOCHIMICA ET COSMOCHIMICA, 2011, 10.1016/j.gca.2010.10.027, Table 5	ips_03_tuff_et_al.csv
Ga	Mo	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Re	Mo	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Mo	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
In	Mo	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv

i	j	$ε_{i}^{j}$	Reference	Source
Al	N	1.685022089	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
As	N	5.198733532	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	N	4.967589379	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
C	N	7.10567279	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	N	2.887292006	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	N	-9.767850348	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	N	2.200887395	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	N	-4.509320877	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	N	-5.02939522	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Al	1.699665833	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	As	5.222258667	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	B	4.999002678	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	C	7.226621513	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Co	2.862412377	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Cr	-9.798690015	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Cu	2.22880759	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Mn	-4.516719056	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Mo	-5.071726027	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	N	0.749208594	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Nb	-26.72752695	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Ni	1.644106969	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	O	-7.207325398	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	P	7.98474696	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	S	1.33744887	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Sb	3.240405299	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Se	1.52430492	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Si	6.058863769	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Sn	2.31011148	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Ta	-45.53796517	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Te	35.18539906	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Ti	-118.3451138	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	V	-23.24034346	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	W	-3.820775099	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Zr	-237.7362139	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	N	-26.69915952	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	N	1.615999167	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	N	-7.340836746	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	N	8.261393553	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	N	1.312898458	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Sb	N	3.234008235	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Se	N	1.541574441	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	N	6.065524104	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Sn	N	2.309431624	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ta	N	-38.83422754	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Te	N	35.04260584	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ti	N	-118.29003	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
V	N	-22.36520666	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
W	N	-3.828112301	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Zr	N	-237.9071289	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	Nb	-22.78075114	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Nb	-1.928370278	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	Nb	2.100362537	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Nb	-26.72752695	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	C	-22.79947109	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	H	-1.928897184	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	Mn	2.090172406	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	N	-26.69915952	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	Nb	-0.663498299	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	O	-46.81159787	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	P	-5.304928924	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	S	-5.508268486	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	Si	-0.661569089	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Nb	-46.65884297	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Nb	-5.263032766	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Nb	-2243.87022	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Nb	-0.663498299	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Nb	0	Tuff, J, Wood, BJ, Wade, J,"The effect of Si on metal-silicate partitioning of siderophile elements and implications for the conditions of core formation", GEOCHIMICA ET COSMOCHIMICA, 2011, 10.1016/j.gca.2010.10.027, Table 5	ips_03_tuff_et_al.csv
Nb	Si	0	Tuff, J, Wood, BJ, Wade, J,"The effect of Si on metal-silicate partitioning of siderophile elements and implications for the conditions of core formation", GEOCHIMICA ET COSMOCHIMICA, 2011, 10.1016/j.gca.2010.10.027, Table 5	ips_03_tuff_et_al.csv
Ga	Nb	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Re	Nb	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Nb	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
In	Nb	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv

i	j	$ε_{i}^{j}$	Reference	Source
C	Ni	2.307261408	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ca	Ni	-10.74532153	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	Ni	-0.002482274	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	Ni	-0.510987776	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	Ni	-1.765618406	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	Ni	1.644106969	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	C	2.307306855	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	Ca	-10.67015196	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	Cr	0.004649947	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	H	-0.515055797	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	Mn	-1.768109487	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	N	1.615999167	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	Ni	0.118590464	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	O	1.373600304	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	P	0.675425224	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	Pb	-4.551205787	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	S	-0.049017199	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	Si	1.192343423	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	Ni	1.401961492	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Ni	0.675525061	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Ni	-4.527498297	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Ni	-0.049552284	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Ni	1.159816015	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Ni	7.5	Tuff, J, Wood, BJ, Wade, J,"The effect of Si on metal-silicate partitioning of siderophile elements and implications for the conditions of core formation", GEOCHIMICA ET COSMOCHIMICA, 2011, 10.1016/j.gca.2010.10.027, Table 5	ips_03_tuff_et_al.csv
Ni	Si	7.5	Tuff, J, Wood, BJ, Wade, J,"The effect of Si on metal-silicate partitioning of siderophile elements and implications for the conditions of core formation", GEOCHIMICA ET COSMOCHIMICA, 2011, 10.1016/j.gca.2010.10.027, Table 5	ips_03_tuff_et_al.csv
Ga	Ni	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Re	Ni	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	Ni	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
In	Ni	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv

i	j	$ε_{i}^{j}$	Reference	Source
Al	P	4.662327989	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
B	P	1.310973128	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
C	P	6.9624642	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	P	0.918217379	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	P	-3.771504784	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	P	-8.276816573	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
H	P	2.362191778	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	P	-6.450570915	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	P	-0.321300468	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
N	P	7.98474696	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Nb	P	-5.304928924	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	P	0.675425224	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
O	P	9.390385756	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Al	4.635548852	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	B	1.31790581	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	C	7.028416149	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Co	0.917334176	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Cr	-3.792267281	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Cu	-8.319075438	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	H	2.354210548	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Mn	-6.463825022	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Mo	-0.322005537	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	N	8.261393553	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Nb	-5.263032766	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Ni	0.675525061	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	O	9.294454798	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	P	7.345820235	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Pb	6.157107511	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	S	4.792205641	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Si	11.9682099	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Sn	5.101319047	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Ti	-7.75626691	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	V	-4.956054565	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	W	-17.62860564	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	P	6.052217495	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	P	4.786614678	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	P	11.94609266	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Sn	P	4.910988775	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ti	P	-7.2217091	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
V	P	-4.921572889	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
W	P	-17.86460627	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ga	P	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Re	P	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
Ge	P	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv
In	P	0	Interaction parameter estimates for unknown elements by J. Wade and B.Wood	ips_04_estimates.csv

i	j	$ε_{i}^{j}$	Reference	Source
Al	Pb	2.770434827	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
C	Pb	5.599250519	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Co	Pb	-0.058380864	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cr	Pb	4.38510411	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Cu	Pb	-7.296821017	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mn	Pb	-5.050408556	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Mo	Pb	-0.743841511	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Ni	Pb	-4.551205787	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
P	Pb	6.157107511	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Al	2.77830688	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	C	5.586849001	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Co	-0.053731221	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Cr	4.359306429	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Cu	-7.278790128	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Mn	-5.057950205	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Mo	-0.717815577	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Ni	-4.527498297	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	P	6.052217495	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	S	-38.55001484	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Si	5.897121543	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	Sn	26.07506319	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pb	W	-2.230497562	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
S	Pb	-38.66571491	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Pb	-10.95764132	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Sn	Pb	26.48256636	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
W	Pb	-2.221592864	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Si	Pb	5.9	Correction to Gordon and Breach IP table. B. Wood, 2013-10-23.	ips_06_corrections.csv
Pb	Si	5.9	Correction to Gordon and Breach IP table. B. Wood, 2013-10-23.	ips_06_corrections.csv
Pb	C	8.75	Revised epsilon values from high pressure experiments, A. Norris DPhil thesis 2016.	ips_08_corrections_norris.csv

HomeInteraction Parameters

Interaction Parameters Matrix ( εij )

Interaction Parameter Orphans

Interaction Parameters - Table

Raw Data By Element

Ag (Silver)

Al (Aluminum)

As (Arsenic)

Au (Gold)

B (Boron)

Be (Beryllium)

C (Carbon)

Ca (Calcium)

Ce (Cerium)

Co (Cobalt)

Cr (Chromium)

Cu (Copper)

Ge (Germanium)

H (Hydrogen)

Hf (Hafnium)

La (Lanthanum)

Mg (Magnesium)

Mn (Manganese)

Mo (Molybdenum)

N (Nitrogen)

Nb (Niobium)

Ni (Nickel)

O (Oxygen)

P (Phosphorus)

Pb (Lead)

Pd (Palladium)

Pt (Platinum)

Interaction Parameters Matrix ( $ε_{i}^{j}$ )

i	j	$ε_{i}^{j}$	Reference	Source
O	Pt	1.128774161	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pt	O	1.129373957	Gordon and Breach, Steelmaking Data Sourcebook, 1984, Table 2.1, p280-293	ips_01_gordon_breach.csv
Pt	S	4